Brand Name : VANFORGE
Certification : ISO9001:2015, ABS, BV, CCS, DNV GL, NKK
Place of Origin : China
MOQ : 5 metric tons
Payment Terms : L/C, T/T
Supply Ability : 3000 metric tons per month
Delivery Time : 15 days
Packaging Details : In bundles, standard seaworthy packing for export
Material : Alloy steel
Process : Hot rolled
Shape : Flat plate
Surface treatment : Plain and smooth
Length : Up to 12000mm
Condition : Quenched and tempered
Application : Molds and tooling
Price : Negotiable
4142H TOOL STEEL (Holderblock) is a prehardened CrMnMo-alloyed tool steel for the construction of plastic molds.
4142H TOOL STEEL is applied by the customers for accessories with such holderblock requirements as ejector plates, supports, clamping plates and housings for diecasting dies. It is characterized by excellent polishability, photoetchability, spark erosion behaviour and dimensional stability as well as good machinability.
Designation and range of application
4142H TOOL STEEL is a modified version of AISI 4142 in holderblock quality.
4142H TOOL STEEL is available as plate with sheared or flame cut edges in the following dimensions:
|Thickness||> 12 ≤ 130 mm||> 1/2 ≤ 5 inch||> 130 ≤ 205 inch||> 5 ≤ 8 inch|
|Width (1)||≥ 1000 ≤ 2500 mm||≥ 40 ≤ 98 1/4 inch||≥ 1000 ≤ 2050 mm||≥ 40 ≤ 80 1/2 inch|
|Length||≥ 4500 ≤ 6000 mm||≥ 177 1/2 ≤ 236 inch||≥ 4000 ≤ 6000 mm||≥ 157 1/2 ≤ 236 inch|
(1) Widths < 1250 mm (49 in) have to be ordered with an even number of plates
Other dimensions available upon request.
The 4142H TOOL STEEL production route is designed to achieve the excellent machinability and dimensional stability of this holderblock steel type. The good oxidic cleanliness and the modification of the few remaining inclusions by the calcium treatment lead to good machinability and minimize the tool wear. 4142H TOOL STEEL should not be applied for photoetching and spark erosion.
These properties can only be achieved by the combination of the following 4142H TOOL STEEL-production steps:
· chemical analysis in dependence of dimensions
· vacuum degassing
· argon stirring for high sulfidic and oxidic cleanliness
· calcium treatment for inclusion shape control
· special casting conditions to assure the high cleanliness and homogenity
· High Shape Factor Rolling (high thickness reduction) to realize a closely packed structure
· appropriate heat treatment parameters according to analysis and dimensions to assure homogeneous hardness distribution over the plate and to minimize residual stresses
For the ladle analysis the following limiting values in % are applicable
4142H TOOL STEEL is supplied in the prehardened (air hardened + tempered) condition.
Mechanical and technological properties in the delivery condition
Unless otherwise agreed the hardness at the surface in the delivery condition is 260 - 310 HB. According to EN 18265, table B2, this corresponds to a tensile strength of approximately 830 - 985 MPa (119 - 142 ksi).
· Heat analysis
· Dimension control
· Surface inspection
The hardness (HB) is tested on surface of each rolled mother plate.
· Ultrasonic testing
Unless otherwise agreed, 100 % ultrasonic testing is performed on each plate in the delivery condition in accordance with ASTM A 578, Level B.
Upon request, an ultrasonic testing in accordance with EN 10160 is possible. As admissible limit apply quality class 3 for thicknesses £ 150 mm (6 in) and quality class 2 in table 5 of EN 10228-3 for thicknesses > 150 mm (6 in). In this case the desired testing type has to be indicated on the order.
Unless otherwise agreed, the results are documented in an inspection certificate 3.1 in accordance with EN 10204.
Identification of plates
Unless otherwise agreed the marking is carried out via steel stamps with at least the following information:
· steel grade (4142H TOOL STEEL)
· heat number
· number of mother plate and individual plate
· the manufacturer’s symbol
· inspector’s sign
4142H TOOL STEEL is delivered in the prehardened condition; therefore further heat treatment is generally not necessary. This avoids the risks and costs involved by the hardening and tempering of a mold after processing. Should a heat treatment become necessary, the following data are recommended:
|soft annealing||stress relieving||Preheating before hardening||hardening||tempering|
700 - 720 °C (1290 - 1330 °F) 2 - 4 h,
hardness about 230 HB
in the delivery condition max.
580 °C (1080 °F)
1 - 2 h,
450 - 650 °C (840 - 1200 °F)
|840 - 860 °C (1540 - 1580 °F)/oil; for low wall thicknesses warm bath hardening at 200 - 230 °C (390 - 450 °F) is possible||in accordance with tempering diagram to required hardness (min. 1 h/25 mm (1 in) wall thickness)|
General technical delivery requirements
Unless otherwise agreed, the general technical delivery requirements in accordance with EN 10021 apply.
Unless otherwise agreed, tolerances are in accordance with EN 10029 / ASTM A 6 with the following restrictions:
|plate thickness:||in accordance with EN 10029, class C / ASTM A 6|
|plate width:||≥1000 mm≤1500 mm||± 25 mm||≥49≤59 in||± 1 in|
|>1500 mm≤2050 mm||± 40 mm||>59≤80 1/2 in||± 1 1/2 in|
|>2050 mm||± 50 mm||>80 1/2 in||± 2 in|
|plate length:||± 1000 mm||± 40 in|
Unless otherwise agreed, short lengths ≥2 m (79 in) are part of the delivery.
Unless otherwise agreed, the specifications will be in accordance with EN 10163-2 class A, subclass 3. Shot blasting of upper and lower surface of the plate and shop priming are possible on request.
If special requirements, which are not listed in this specification, are to be met by the steel due to its intended use or processing, these requirements are to be agreed before placing the order.
4142H CrMnMo High Mechanical Hr Steel Plate Anti Corrosion For Molds Tooling Images